Ispitivanje korozijske otpornosti alatnih čelika za hladni rad u mediju 3,5 % NaCl

diplomski rad

• Autor: Kristina Brodarac
• Mentor: Anita Begić Hadžipašić (mentor)
• Mentor: Sandra Brajčinović (pomoć pri izradi, neposredni voditelj)
• Član povjerenstva: Ljerka Slokar Benić (predsjednik povjerenstva)
• Član povjerenstva: Anita Begić Hadžipašić (član povjerenstva)
• Član povjerenstva: Stjepan Kožuh (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2021-09-28, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

U ovom radu provedeno je ispitivanje korozijske otpornosti različitih uzoraka alatnih čelika za hladni rad u mediju vodovodne vode i otopine 3,5 % NaCl pomoću elektrokemijskih metoda. Tafelovom ekstrapolacijom polarizacijskih krivulja dobivena je manja brzina korozije za alatni čelik oznake K340, što dovodi do činjenice da je ispitani uzorak korozijski otporniji od alatnog čelika oznake K100. O tome svjedoče i rezultati impedancijskih mjerenja pomoću kojih je dobiven veći otpor prijenosa naboja za uzorak oznake K340. To znači da se na uzorku oznake K340 formirao deblji zaštitni sloj koji je imao ulogu barijere prodiranju agresivnog kloridnog medija. Nagrizanjem u nitalu vidljiva je mikrostruktura koja se sastoji od ledeburitne metalne osnove i karbida. Uzorak alatnog čelika oznake K340 ima sitnozrnatu strukturu karbida te je zbog toga i korozijski otporniji od uzorka alatnog čelika oznake K100 čija je struktura karbida krupnozrnata. Svjetlosnim mikroskopom nakon elektrokemijskih ispitivanja u 3,5 % NaCl dobivena je metalografska slika oba uzorka iz koje je vidljivo da je uzorak alatnog čelika oznake K100 više korodirao, dok je uzorak alatnog čelika oznake K340 stvorio znatno manji korozijski sloj i to samo uz rubove uzorka. U skladu s dobivenim rezultatima može se zaključiti da se alatni čelik K340 pokazao korozijski otpornijim i u vodi i u kloridnom mediju.

Sažetak (engleski)

In this paper, the corrosion resistance of different samples of tool steels for cold work in a medium of tap water and 3.5 % NaCl solution was performed using electrochemical methods. Tafel extrapolation of polarization curves resulted in a lower corrosion rate for K340 tool steel, which leads to the fact that the tested sample is more corrosion resistant than K100 tool steel. This is evidenced by the results of impedance measurements, which obtained a higher charge transfer resistance for the sample marked K340. This means that a thicker protective layer was formed on the sample marked K340, which acted as a barrier to the penetration of the aggressive chloride medium. Corrosion in the nital reveals a microstructure consisting of a ledeburite metal base and carbide. The K340 tool steel sample has a fine-grained carbide structure and is therefore more corrosion-resistant than the K100 tool steel sample, whose coarbide structure is coarse-grained. Using a light microscope after electrochemical tests in 3.5 % NaCl, a metallographic image of both samples was obtained, which shows that the K100 tool steel sample corroded more, while the K340 tool steel sample created a significantly smaller corrosion layer and only along the edges of the sample. In accordance with the obtained results, it can be concluded that K340 tool steel proved to be more corrosion resistant in both water and chloride medium.

• Ključne riječi: alatni čelici za hladni rad; brzina korozije; impedancija; 3; 5 % NaCl; mikrostruktura
• Ključne riječi (engleski): tool steels for cold work; corrosion rate; impedance; 3; 5 % NaCl; microstructure
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:797467
• Studijski program: Naziv: Metalurgija; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka metalurgije (mag. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2021-10-06 10:03:31