Karakterizacija mikrostrukture sinterirane titan-niobij legure za biomedicinsku primjenu

diplomski rad

• Naslov (engleski): Characterization of microstructure of sintered titanium-niobium alloy for biomedical application
• Autor: Gorana Domitrović
• Mentor: Ljerka Slokar Benić (mentor)
• Član povjerenstva: Stjepan Kožuh (predsjednik povjerenstva)
• Član povjerenstva: Ljerka Slokar Benić (član povjerenstva)
• Član povjerenstva: Martina Lovrenić-Jugović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2019-09-26, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

Legure titana, zbog svojih povoljnih svojstava, pronalaze sve veću primjenu u
biomedicini. Međutim, zbog njihove visoke cijene, danas se sve više razvijaju i koriste nove
metode s ciljem proizvodnje ekonomičnijih legura. Stoga je u okivru ovog rada za
proizvodnju legure Ti80Nb20 korištena tehnologija metalurgije praha.
Istraživana titan-niobij legura pripravljena je iz elementarnih prahova miješanjem
odnosno mehaničkim legiranjem u kugličnom mlinu. Nakon toga je iz smjese izdvojeno 8
uzoraka koji su prešani na hidrauličnoj preši, te sinterirani u cijevnoj peći u zaštitnoj atomsferi
argona. Mikrostruktura sinteriranih uzoraka je karakterizirana različitim metodama kako bi se
utvrdili optimalni tehnološki parametri za postizanje mikrostrukture sa zadovoljavajućim
karakteristikama za primjenu u biomedicini.
Dobiveni rezultati pokazuju da je uz malu korekciju primijenjenih tehnoloških
parametara, u smislu produžavanja vremena miješanja/mehaničkog legiranja, primijenjenom
tehnologijom metalurgije praha moguće ekonomično proizvesti Ti80Nb20 leguru sa svojstvima
povoljnim za biomedicinsku primjenu.

Sažetak (engleski)

Due to their favourably properties, titanium alloys are increasingly used in
biomedicine. However, because of their high cost, new methods are being developed and used
today to produce more economical alloys. Therefore, in the frame of this work, powder
metallurgy was used to produce Ti80Nb20 alloy.
The investigated titanium-niobium alloy was prepared from elemental powders by
mixing i.e. mechanical alloying in a ball mill. After that, 8 samples singled out from the
mixture were pressed on a hydraulic press and sintered in a tube furnace in a protective
atmosphere of argon. For the characterization of the microstructure of sintered samples
various methods were applied to determine the optimal technological parameters for
achieving microstructure with satisfactory characteristics for biomedical applications.
The obtained results show that with a small correction of the applied technological
parameters, in terms of time extension of mixing/mechanical alloying, it is possible to
economically produce Ti80Nb20 alloy with properties suitable for biomedical application by
using powder metallurgy technology.

• Ključne riječi: legure titana; metalurgija praha; mikrostruktura; tvrdoća
• Ključne riječi (engleski): titanium alloys; powder metallurgy; microstructure; hardness
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:377325
• Studijski program: Naziv: Metalurgija; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka metalurgije (mag. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2019-10-11 11:08:30