Lijevanje i karakterizacija binarne 50Cu-50Zr legure

završni rad

• Naslov (engleski): Casting and characterisation of binary 50Cu-50Zr alloy
• Autor: Mihovil Bilanović
• Mentor: Ivana Ivanić (mentor)
• Član povjerenstva: Stjepan Kožuh (predsjednik povjerenstva)
• Član povjerenstva: Ivana Ivanić (član povjerenstva)
• Član povjerenstva: Zoran Glavaš (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2022-09-30, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija; Procesna metalurgija

Sažetak

U ovom radu istraživana je binarna 50Cu-50Zr legura koja je služila kao predlegura za daljnji
postupak mikrolegiranja CuAlMn legure s prisjetljivosti oblika s cirkonijem. Predlegura Cu-Zr
dobivena je postupkom taljenja čistih metala u elektrolučnoj peći i lijevanja u cilindrične kalupe
promjera 8 mm i duljine 12 mm. Termodinamički proračun faznog dijagrama proveden je
Thermo-Calc programom, na osnovi pripremljene baze termodinamičkih podataka prema
optimiziranim literaturnim podacima te je utvrđeno da pripremljena predlegura pri sastavu 50
% Cu i 50 % Zr ima temperaturu solidusa 851 °C što je povoljna vrijednost za daljnju primjenu.
Mikrostrukturna analiza pokazala je dvofaznu mikrostrukturu, što je i u korelaciji s dobivenim
termodinamičkim proračunom.

Sažetak (engleski)

In this work, the 50Cu-50Zr binary alloy was studied, which served as a master alloy for the
further process of microalloying the CuAlMn shape memory alloy with zirconium. The Cu-Zr
master alloy was obtained by melting pure metals in an electric arc furnace and casting into
cylindrical molds with a diameter of 8 mm and a length of 12 mm. The thermodynamic
calculation of the phase diagram was performed using the Thermo-Calc program based on a
prepared database of thermodynamic data according to optimized literature data, and it was
found that the produced master alloy with a composition of 50 % Cu and 50 % Zr has a solidus
temperature of 851 °C, which is a favorable value for further application. The microstructural
analysis revealed a two-phase microstructure, which correlates with the thermodynamic
calculations obtained.

• Ključne riječi: Cu-Zr legura; mikrostruktura; termodinamički proračun
• Ključne riječi (engleski): Cu-Zr alloy; microstructure; thermodynamic calculation
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:986577
• Studijski program: Naziv: Ljevarstvo; Vrsta studija: stručni; Stupanj studija: kratki; Akademski / stručni naziv: stručni/a pristupnik/ pristupnica ljevarstva (pristup.ljev.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2022-09-29 12:20:49