Termodinamičko modeliranje Cu-Al-Mn legura

diplomski rad

• Naslov (engleski): Thermodynamic modelling of Cu-Al-Mn alloys
• Autor: Monika Knežević
• Mentor: Tamara Holjevac-Grgurić (mentor)
• Član povjerenstva: Mirko Gojić (predsjednik povjerenstva)
• Član povjerenstva: Tamara Holjevac-Grgurić (član povjerenstva)
• Član povjerenstva: Stjepan Kožuh (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2017-10-13, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

Cu-Al-Mn legure danas se često koriste u biomedicini, elektroindustriji, avioindustriji i dr.
kao materijali s prisjetljivosti oblika. U ovom radu istraživane su ternarne Cu-Al-Mn legure, s
različitim udjelima aluminija i mangana, u području bogatom bakrom. Legure su pripremljene
u elektrolučnoj peći te su zatim uzorci odliveni u cilindrične kalupe promjera 8 mm i duljine
12 mm. Nakon pripreme uzoraka brušenjem i poliranjem, analiza je provedena optičkom
mikroskopijom i pretražnom elektronskom mikroskopijom, uz analizu kemijskog sastava
energetsko disperzijskom spektroskopijom. Toplinska analiza provedena je na STA DSC/TG
uređaju te su određene temperature transformacija u rasponu od 25 °C do 1150 °C.
Termodinamički proračun faznog dijagrama proveden je Thermo-Calc programom, na osnovi
pripremljene baze termodinamičkih podataka prema optimiziranim literaturnim podacima.
Rezultati termodinamičkog proračuna korelirani su s rezultatima ispitivanja mikrostrukture i
toplinske analize.

Sažetak (engleski)

Cu-Al-Mn alloys are often used in biomedicine, electro-industry, aerospace, etc., mostly as
shape memory alloys. In this paper, Cu-Al-Mn ternary alloys with different content of
aluminium and manganese, in the Cu-rich corner were investigated. Alloys were prepared in
the electric-arc furnace and then casted in the cylindrical mould with dimensions of diameter
8mm and length 12mm. After grinding and polishing, samples were analyzed by optical
microscopy and scanning electron microscopy, equipped by energy dispersive spectroscopy.
Thermal analysis was performed by STA DSC/TG and phase transformation temperatures
were determined in the interval from 25 °C to 1150 °C. Thermodynamic calculations were
performed by Thermo-Calc software, with prepared database according to optimized
parameters. Results of the thermodynamic calculations were correlated with results of
microstructure analysis and thermal analysis.

• Ključne riječi: Cu-Al-Mn legure; mikrostruktura; toplinska analiza; termodinamički proračun
• Ključne riječi (engleski): Cu-Al-Mn alloys; microstructure; thermal analysis; thermodynamic calculation
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:874203
• Studijski program: Naziv: Metalurgija; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka metalurgije (mag. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2017-11-07 11:29:43