prikaz prve stranice dokumenta Properties of continuously casted Cu-Al alloy
  Preuzmi
PDF 2.83 MB
Znanstveni rad - Izvorni znanstveni rad
Properties of continuously casted Cu-Al alloy
U: Proceedings Book 17th International Foundrymen Conference. / Dolić, Natalija; Zovko Brodarac, Zdenka; Begić Hadžipašić, Anita (ur.). Sisak: Sveučilište u Zagrebu Metalurški fakultet, 2018. str. 292-302. urn:nbn:hr:115:022103
Kožuh, Stjepan; Džomba, Vlado; Holjevac Grgurić, Tamara; Jandrlić, Ivan; Kosec, Borut; Gojić, Mirko

Citirajte ovaj rad

Kožuh, S., Džomba, V., Holjevac Grgurić, T., Jandrlić, I., Kosec, B. i Gojić, M. (2018). Properties of continuously casted Cu-Al alloy. U N. Dolić, (Ur.), Z. Zovko Brodarac, (Ur.), A. Begić Hadžipašić, (Ur.), Proceedings Book 17th International Foundrymen Conference (str. 292-302). Sisak: Sveučilište u Zagrebu Metalurški fakultet. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:115:022103

Kožuh, Stjepan, et al. "Properties of continuously casted Cu-Al alloy." Proceedings Book 17th International Foundrymen Conference, Ur. Natalija Dolić, Ur. Zdenka Zovko Brodarac, Ur. Anita Begić Hadžipašić, Sveučilište u Zagrebu Metalurški fakultet, 2018, str. 292-302. https://urn.nsk.hr/urn:nbn:hr:115:022103

Kožuh, Stjepan, Vlado Džomba, Tamara Holjevac Grgurić, Ivan Jandrlić, Borut Kosec i Mirko Gojić. "Properties of continuously casted Cu-Al alloy." U Proceedings Book 17th International Foundrymen Conference, 292-302. Sisak: Sveučilište u Zagrebu Metalurški fakultet, 2018. Citirano 21.10.2024.. https://urn.nsk.hr/urn:nbn:hr:115:022103

Kožuh, S., et al. (2018) 'Properties of continuously casted Cu-Al alloy', u Dolić, N. (ur.), Zovko Brodarac, Z. (ur.), Begić Hadžipašić, A. (ur.), Proceedings Book 17th International Foundrymen Conference, Sveučilište u Zagrebu Metalurški fakultet, Sisak, str. 292-302. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:115:022103 (Datum pristupa: 21.10.2024.)

Kožuh S, Džomba V, Holjevac Grgurić T, Jandrlić I, Kosec B, Gojić M. Properties of continuously casted Cu-Al alloy. U: N. Dolić, ur., Z. Zovko Brodarac, ur., A. Begić Hadžipašić, ur. Proceedings Book 17th International Foundrymen Conference. Sisak: Sveučilište u Zagrebu Metalurški fakultet; 2018. Str. 292-302. [pristupljeno 21.10.2024.] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:022103

S. Kožuh, V. Džomba, T. Holjevac Grgurić, I. Jandrlić, B. Kosec i M. Gojić, "Properties of continuously casted Cu-Al alloy", Proceedings Book 17th International Foundrymen Conference, N. Dolić, Z. Zovko Brodarac i A. Begić Hadžipašić, Ur. Sisak: Sveučilište u Zagrebu Metalurški fakultet, 2018. [Online] Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:022103 [Citirano: 21.10.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:115:022103
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Properties of continuously casted Cu-Al alloy
AutorStjepan Kožuh
AutorVlado Džomba
AutorTamara Holjevac Grgurić
AutorIvan Jandrlić
AutorBorut Kosec
AutorMirko Gojić
UrednikNatalija Dolić
UrednikZdenka Zovko Brodarac
UrednikAnita Begić Hadžipašić
Autorova ustanovaSveučilište u Zagrebu
Metalurški fakultet
(Zavod za fizičku metalurgiju)
(Laboratorij za razvoj i primjenu materijala)
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Metalurgija
Fizička metalurgija
Sažetak (engleski)
In this work are shown properties of continuously casted Cu – 9.1Al alloy before and after heat treatment. The continuously cast cylindrical bar with 8 mm diameter was produced using the device for the vertical continuous casting which is connected with the vacuum induction furnace. Heat treatment was consisted of annealing at 900 °C/30 minutes and water quenching. Microstructural analysis was performed by optical microscopy (OM), scanning electron microscopy (SEM) equipped by device for energy dispersive spectroscopy (EDS) and using differential scanning calorimeter (DSC). Also, hardness and mechanical properties were measured. EDS analysis confirmed that as-cast state of Cu – 9.1Al alloy is successfully done and alloy with homogeneous composition was produced. Optical and scanning electron microscopy showed existence of dual-phase α+β microstructure, which keeps after heat treatment but with certain sporadic changes of α - phase shape. DSC analysis on all samples presented one endothermic change of the heat flow during the heating, which probably represents α→β transformation and one exothermic change of the heat flow during the cooling which probably represents β→α transformation. The effect of heat treatment on the hardness and yield strength values is insignificant, while the tensile strength decreases with annealing.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov zbornikaProceedings Book 17th International Foundrymen Conference
Brojčani podacistr. 292-302
ISBN978-953-7082-31-4
URN:NBNurn:nbn:hr:115:022103
Datum objave publikacije2018
SkupNaziv: Hi-tech casting solution and knowledge based engineering
Lokacija: Opatija, Hrvatska
Organizator: Sveučilište u Zagrebu Metalurški fakultet
Datum početka: 2018-05-16
Datum završetka: 2018-05-18
Vrsta izlaganja: Predavanje
Vrsta resursaTekst
IzdavačSveučilište u Zagrebu Metalurški fakultet