prikaz prve stranice dokumenta Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy
  Preuzmi
PDF 6.4 MB
Znanstveni rad - Izvorni znanstveni rad
Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy
International scientific journal Innovations, 11 (2023), 2; 73-76. urn:nbn:hr:115:630842
Slokar Benić, Ljerka; Komljenović, Luka; Erman, Žiga; Jajčinović, Magdalena

Citirajte ovaj rad

Slokar Benić, Lj., Komljenović, L., Erman, Ž. i Jajčinović, M. (2023). Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy. International scientific journal Innovations, 11. (2), 73-76. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:115:630842

Slokar Benić, Ljerka, et al. "Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy." International scientific journal Innovations, vol. 11, br. 2, 2023, str. 73-76. https://urn.nsk.hr/urn:nbn:hr:115:630842

Slokar Benić, Ljerka, Luka Komljenović, Žiga Erman i Magdalena Jajčinović. "Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy." International scientific journal Innovations 11, br. 2 (2023): 73-76. https://urn.nsk.hr/urn:nbn:hr:115:630842

Slokar Benić, Lj., et al. (2023) 'Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy', International scientific journal Innovations, 11(2), str. 73-76. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:115:630842 (Datum pristupa: 24.04.2024.)

Slokar Benić Lj, Komljenović L, Erman Ž, Jajčinović M. Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy. International scientific journal Innovations [Internet]. 06.2023. [pristupljeno 24.04.2024.];11(2):73-76. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:630842

Lj. Slokar Benić, L. Komljenović, Ž. Erman i M. Jajčinović, "Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy", International scientific journal Innovations, vol. 11, br. 2, str. 73-76, Lipanj 2023. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:630842. [Citirano: 24.04.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:115:630842
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Analysis of the densification of a biomedical titanium alloy produced by powder metallurgy
AutorLjerka Slokar Benić
AutorLuka Komljenović
AutorŽiga Erman
AutorMagdalena Jajčinović
Autorova ustanovaSveučilište u Zagrebu
Metalurški fakultet
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Metalurgija
Sažetak (engleski)
Titanium as a raw material for production is very expensive due to its high price and the complex production process. One of the successful alternatives for the production of titanium alloys and final products is powder metallurgy technology. In this work, a Ti-20Zr alloy for biomedical applications was produced using the powder metallurgy process. The density values determined for the compacts depend on the compression pressure. Namely, the compressibility of the powder mixture increases with increasing compaction pressure. A higher sintering temperature as well as a longer sintering time are more favourable to obtain higher values for the sintered density. Similarly, the compression coefficient is lower for samples compacted at higher pressure, while its value increases with increasing sintering temperature. The volume change in the volume of the sample is more pronounced after sintering at higher temperature and shorter time.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - međunarodna recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaInternational scientific journal Innovations
Brojčani podacivol. 11, br. 2, str. 73-76
p-ISSN2603-3763
e-ISSN2603-3771
URN:NBNurn:nbn:hr:115:630842
Datum objave publikacije2023-06
URL dokumentahttp://bib.irb.hr/1281518
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2023-07-05 10:41:37