Influence of medium on corrosion and microstructural properties of HTCS-130 tool steel for hot work

Scientific paper - Original scientific paper

• Author: Sandra Brajčinović
• Author: Anita Begić Hadžipašić
• Author: Jožef Medved
• Author: Stjepan Kožuh
• Author's institution: University of Zagreb; Faculty of Metallurgy
• Scientific / art field, discipline and subdiscipline: TECHNICAL SCIENCES; Metallurgy

Abstract (english)

In this paper the corrosion resistance of tool steel for hot work in the industrial emulsion medium (Lenox Band-Ade semi-synthetic oil + water, in ratio 1:10), water and 3.5% NaCl medium was tested. By Tafel’s extrapolation from polarization curves it was established that the tested tool steel showed extremely high corrosion rate in water and 3.5% NaCl medium in contrast to medium of Lenox BandAde emulsion. The double higher corrosion rate of tool steel is recorded in the chloride medium as opposed to that obtained in water, indicating that the tested steel is more corrosion resistant in water. The obtained results were confirmed by the method of electrochemical impedance spectroscopy. The sample of tool steel in the Lenox Band-Ade emulsion medium showed far greater value of charge transfer resistance Rct than that obtained in the water medium and 3.5% NaCl, which means that the Lenox Band-Ade emulsion formed a thicker oxide layer that has the role of barrier in further penetration of aggressive ions from the solution. The conducted SEM analysis after electrochemical measurements in 3.5% NaCl medium indicate the occurrence of pitting corrosion caused by breaking the passive surface of the material as a result of the action of aggressive ions from the solution. The EDS analysis of formed pits has been shown the increased oxygen content, but also the higher presence of sodium and chlorine, which accumulate in the pits, and come from the medium. Molybdenum and tungsten showed the highest presence in white deposits on the sample surface, which represent parts that did not completely cover with oxide layer, which is why the smallest oxygen content was recorded at these sites. The obtained corrosion rate values in the water medium and the chloride medium indicate that the studied tool steel is poorly stable in water and chloride media, and because of that it can only be used in exceptional cases under conditions in which it will come into contact with water or chloride medium.

• Keywords (english): tool steel for hot work; pitting corrosion; corrosion rate; impedance; microstructure
• Language: english
• Publication type: Scientific paper - Original scientific paper
• Publication status: Published
• Peer review: Peer review - international
• Publication version: Published version
• Publication title: 18th International Foundrymen Conference Coexistence of material science and sustainable technology in economic growth
• Numbering: pp. 188-205
• ISBN: 978-953-7082-34-5
• URN:NBN: urn:nbn:hr:115:433032
• Publication: 2019
• Project: Number: KK.01.1.1.02.0020; Title (croatian): Centar za ljevarstvo - SIMET; Title (english): Center for casting - SIMET; Acronym: SIMET; Leader: Zdenka Zovko Brodarac; Jurisdiction: Croatia; Funding stream: European Regional Development Fund
• Conference: Title: 18th International Foundrymen Conference Coexistence of material science and sustainable technology in economic growth; Location: Sisak, Croatia; Start date: 2019-05-15; End date: 2019-05-17; Assembly type: Lecture
• Document URL: http://bib.irb.hr/1002275
• Type of resource: Text
• Publisher: University of Zagreb Faculty of Metallurgy
• Publishing place: Sisak
• Access conditions: Open access
• Created on: 2019-05-22 08:29:58