prikaz prve stranice dokumenta Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
  Preuzmi
PDF 2.7 MB
Znanstveni rad - Izvorni znanstveni rad
Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
Engineering Power : Bulletin of the Croatian Academy of Engineering, 17 (2022), 3; 19-27. urn:nbn:hr:115:096503
Begić Hadžipašić, Anita; Brajčinović, Sandra; Rajković, Marija

Citirajte ovaj rad

Begić Hadžipašić, A., Brajčinović, S. i Rajković, M. (2022). Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium. Engineering Power : Bulletin of the Croatian Academy of Engineering, 17. (3), 19-27. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, Anita, et al. "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium." Engineering Power : Bulletin of the Croatian Academy of Engineering, vol. 17, br. 3, 2022, str. 19-27. https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, Anita, Sandra Brajčinović i Marija Rajković. "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium." Engineering Power : Bulletin of the Croatian Academy of Engineering 17, br. 3 (2022): 19-27. https://urn.nsk.hr/urn:nbn:hr:115:096503

Begić Hadžipašić, A., Brajčinović, S. i Rajković, M. (2022) 'Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium', Engineering Power : Bulletin of the Croatian Academy of Engineering, 17(3), str. 19-27. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:115:096503 (Datum pristupa: 02.12.2024.)

Begić Hadžipašić A, Brajčinović S, Rajković M. Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium. Engineering Power : Bulletin of the Croatian Academy of Engineering [Internet]. 2022. [pristupljeno 02.12.2024.];17(3):19-27. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:096503

A. Begić Hadžipašić, S. Brajčinović i M. Rajković, "Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium", Engineering Power : Bulletin of the Croatian Academy of Engineering, vol. 17, br. 3, str. 19-27, 2022. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:115:096503. [Citirano: 02.12.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:115:096503
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Influence of microstructure on the resistance of tool steels to local corrosion in 3.5% NaCl medium
AutorAnita Begić Hadžipašić
AutorSandra Brajčinović
AutorMarija Rajković
Autorova ustanovaSveučilište u Zagrebu
Metalurški fakultet
Znanstveno / umjetničko
područje, polje i grana		TEHNIČKE ZNANOSTI
Metalurgija
Sažetak (engleski)
In this research, electrochemical and metallographic tests were carried out on tool steel for cold and hot work, as well as steel for cementation, with the goal to obtain corrosion parameters to determine which of the examined samples is more resistant to local pitting corrosion. Electrochemical tests were performed in a medium of 3.5% NaCl, and were based on conducting cyclic anodic polarization in the potential range from -2000 mV to 200 mV vs SCE and vice versa. The results of the research showed that all three samples are subject to pitting corrosion, but the worst was the cementing tool steel sample X19NiCrMo4, which had the lowest pitting potential. The W600 tool steel sample for hot work proved to be the best, with the highest pitting potential. The results of the electrochemical tests coincide with the metallographic tests, because after corrosion in the chloride medium only the beginnings of pitting corrosion are visible on the surface of the W600 sample in the form of partial accumulations of corrosion products, while the X19NiCrMo4 cementing steel sample was completely covered with corrosion products, which means that of the three tested tool steels, cementing steel is the most susceptible to pitting corrosion and is not recommended for use in conditions where it comes into contact with chloride ions. The martensitic microstructure of cementing tool steel is responsible for the very low pitting potential and, consequently, pronounced pitting corrosion. On the other hand, the W600 tool steel showed better corrosion resistance due to its finer grain and uniform carbide distribution.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran - domaća recenzija
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaEngineering Power : Bulletin of the Croatian Academy of Engineering
Brojčani podacivol. 17, br. 3, str. 19-27
p-ISSN1331-7210
URN:NBNurn:nbn:hr:115:096503
Datum objave publikacije2022
ProjektŠifra: KK.01.1.1.02.0020
Naziv (hrvatski): Centar za ljevarstvo - SIMET
Naziv (engleski): Center for casting - SIMET
Kratica: SIMET
Voditelj: Zdenka Zovko Brodarac
Pravna nadležnost: Hrvatska
Financijer: Europska komisija
Linija financiranja: European Regional Development Fund
ProjektŠifra: KK.01.1.1.02.0022
Naziv (hrvatski): Virtulab – Integrirani laboratorij za primarne i sekundarne sirovine
Kratica: Virtulab
Voditelj: Sibila Borojević Šoštarić
Pravna nadležnost: Hrvatska
Financijer: Europska komisija
Linija financiranja: European Regional Development Fund
URL dokumentahttps://hrcak.srce.hr/clanak/435996
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2024-04-29 10:59:51