Utjecaj kemijskog sastava i cijepljenja na mikrostrukturne značajke i mehanička svojstva nodularnog lijeva

diplomski rad

• Naslov (engleski): Influence of chemical composition and inoculation on microstructural features and mechanical properties of ductile iron
• Autor: Luka Voloder
• Mentor: Zdenka Zovko Brodarac (mentor)
• Član povjerenstva: Zoran Glavaš (predsjednik povjerenstva)
• Član povjerenstva: Zdenka Zovko Brodarac (član povjerenstva)
• Član povjerenstva: Ladislav Lazić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2016-09-30, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija; Procesna metalurgija

Sažetak

Nodularni ljev je pronašao široku primjenu u mnogim granama industrije zahvaljujući
izvrsnim performansama. Svojstva nodularnog lijeva često su predodređena razvojem
mikrostrukture na koju osim uvjeta skrućivanja utječu kemijski sastav i metalurška obrada
taline. Metalurška obrada taline cijepljenjem predstavlja način kontrole strukture i mehaničkih
svojstava željeznih lijevova putem minimalizacije pothlađenja i povećanja broja grafitnih
nodula tijekom skrućivanja. U ovom radu ispitani su utjecaj kemijskog sastava te vrste i
udjela cjepiva na mikrostrukturu i mehanička svojstva odljevaka od nodularnog lijeva
kvalitete EN GJS 400–18–LT. Radi proučavanja utjecaja obrade taline i dobivenog kemijskog
sastava pomno su odabrana cjepiva i nodulatori iz Elkemove palete proizvoda. Tako su
primjenjene razne kombinacije cjepiva Barinoc, Top-seed, Alinoc te nodulatora Elmag 5800 i
Lamet 5836 te u pojedinim slučajevima primjenjeno je alternativno cjepivo Ten-blok. Sve
kombinacije povoljno su utjecale na razvoj grafita u obliku nodula i visokočvrste feritne
metalne osnove. Prepoznate su najpovoljnije kombinacije cjepiva i nodulatora za razvoj
mikrostrukture i svojstava odljevaka poput Elmag 5800 i Barinoc te Lamet 5836 i Top-seed.

Sažetak (engleski)

Ductile cast iron has found wide application in many industries due to its excellent
performance. The properties of ductile cast iron are often deterministic for the microstructure
development. Beside solidification condition, chemical composition and metallurgical melt
treatment directly influence on microstructure development. Melt treatment by inoculation
represents the way of microstructure and mechanical properties control by minimizing
undercooling and increasing the number of graphite nodules during solidification. In this
study the effect of the chemical composition and inoculants types and its ratio on the
microstructure and mechanical properties development of EN GJS 400-18 - LT quality ductile
iron castings was investigated. In order to study the impact of melt treatment and resulting
chemical composition, selected inoculants and nodulising agents from the Elkem range of
products were choosen. Various particular combinations of inoculants Barinoc, Top-seed,
Alinoc and nodulising agents Elmag 5800, and Lamet 5836, and in some cases, an alternative
inoculant Ten-block were applied. All combinations favorably influenced on graphite
development in the form of nodules and high-strength ferrite metal base. The best
combination of microstructure and casting properties development has been recognized when
combination of inoculants and nodulising agent ELMAG 5800 and Barinoc, as well as Lamet
5836 and Top-seed were applied.

• Ključne riječi: nodularni ljev; obrada taline; mikrostruktura; mehanička svojstva
• Ključne riječi (engleski): ductile iron; melt treatment; microstructure; mechanical properties
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:633782
• Studijski program: Naziv: Metalurgija; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka metalurgije (mag. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2016-10-05 06:44:35