Fizikalna priroda deformacije kod hladne plastične deformacije

diplomski rad

• Naslov (engleski): Physical nature of deformation during cold plastic deformation
• Autor: Tomislav Polak
• Mentor: Tin Brlić (mentor)
• Član povjerenstva: Ljerka Slokar Benić (predsjednik povjerenstva)
• Član povjerenstva: Tin Brlić (član povjerenstva)
• Član povjerenstva: Stjepan Kožuh (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2025-02-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

Poznavanje fizikalne prirode deformacije ima veliku važnost u razumijevanju procesa koji se odvijaju u metalnim materijalima tijekom plastične deformacije. Pritom mikrostrukturne promjene imaju utjecaj na iznose i raspodjelu naprezanja i deformacija čije poznavanje ima ključnu važnost kod oblikovanja deformiranjem metalnih materijala. U ovom radu provedena su istraživanja promjena mikrostrukture niskougljičnog čelika tijekom hladne plastične deformacije. Ispitivanja su provedena istovremenim korištenjem metoda statičkog vlačnog ispitivanja, termografije i digitalne korelacije slike (DIC). Uz navedene metode korištene su metode za analizu mikrostrukture odnosno svjetlosni i transmisijski elektronski mikroskop (TEM). Detaljnija analiza mikrostrukture i dislokacija tijekom hladne plastične deformacije provedena je korištenjem dva različita operacijska moda TEM - a i skenirajućeg TEM - a (STEM). Promjene temperature (naprezanja), deformacije i brzine deformacije u zoni deformacije dobivene metodama termografije i DIC tijekom statičkog vlačnog ispitivanja odnosno plastične deformacije povezane su s promjenama u mikrostrukturi dobivenim metalografskom analizom na svjetlosnom mikroskopu i transmisijskom elektronskom mikroskopu. Tijekom promatranja mikrostrukture naglasak je bio na analizi gustoće dislokacija tijekom plastične deformacije. Identificirane su mikrostrukturne promjene koje se javljaju tijekom hladne plastične deformacije. Utvrđena su mjesta najznačajnijeg očvršćavanja i gustoće dislokacija tijekom hladne deformacije niskougljičnog čelika.

Sažetak (engleski)

The knowledge of the physical nature of deformation is of great importance in understanding the processes that occur in metallic materials during plastic deformation. Microstructural changes have an impact on the stress and strain amounts and distribution which is of key importance in metal forming. In this work, research was conducted on microstructure changes of low-carbon steel during cold plastic deformation. The tests were carried out using the methods of static tensile testing, thermography and digital image correlation (DIC). In addition to the above methods, for microstructure analysis were used: light and transmission electron microscope (TEM). A more detailed analysis of the microstructure and dislocations during cold plastic deformation was carried out using two different operating modes of TEM and scanning TEM (STEM). Changes in temperature (stress), strain and strain rate in the deformation zone, obtained by the methods of thermography and DIC during static tensile testing (plastic deformation), are related to the microstructure changes obtained by metallographic analysis on a light microscope and a transmission electron microscope. The emphasis was on the analysis of dislocation density during plastic deformation. Microstructural changes that occur during cold plastic deformation were identified. The locations of the most significant hardening and dislocation density during cold deformation of low-carbon steel were determined.

• Ključne riječi: hladna plastična deformacija; mikrostruktura; niskougljični čelik; naprezanje; deformacije; dislokacije
• Ključne riječi (engleski): cold plastic deformation; microstructure; low-carbon steel; stress; strain; dislocations
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:054127
• Studijski program: Naziv: Metalurgija; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra inženjer/inženjerka metalurgije (mag. ing. met.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2026-02-24
• Datum i vrijeme pohrane: 2025-02-17 10:15:47