Utjecaj zadržavanja taline nakon obrade na konačnu kvalitetu nodularnog lijeva HR GJS 400-15

završni rad

• Naslov (engleski): Effect of melt retention after treatment on the final quality of nodular cast iron HR GJS 400-15
• Autor: Matija Kuzmić
• Mentor: Ivan Jandrlić (mentor)
• Mentor: Zdenka Zovko Brodarac (sumentor)
• Član povjerenstva: Natalija Dolić (predsjednik povjerenstva)
• Član povjerenstva: Zdenka Zovko Brodarac (član povjerenstva)
• Član povjerenstva: Ivan Jandrlić (član povjerenstva)
• Član povjerenstva: Zoran Glavaš (član povjerenstva)
• Član povjerenstva: Anita Begić Hadžipašić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Metalurški fakultet; Sisak
• Datum i država obrane: 2024-07-10, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: TEHNIČKE ZNANOSTI; Metalurgija

Sažetak

Nodularni lijev HRN-EN-GJS-400-15 koristi se u automobilskoj industriji za izradu dijelova poput zupčanika, diferencijala i osovina zbog svoje visoke čvrstoće i dobre žilavosti.
Konstantnim rastom potražnje kupci postavljaju sve veće zahtjeve za kvalitetnijim proizvodima. Da bi proizvođači to ispunili, važno je konstantno kontrolirati kemijski sastav, minimalizirati eventualne greške u mikrostrukturi i modificirati postupke proizvodnje. U ovom završnom radu prati se proizvodnja odljevaka iz HRN-EN-GJS-400-15, točnije utjecaj vremena zadržavanja taline nakon obrade u loncu na konačnu kvalitetu nodularnog lijeva. U procesu proizvodnje odlivene su dvije Y probe na kojima su provedena ispitivanja. Provedena su ispitivanja kemijskog sastava, mehaničkih svojstava i strukture nodularnog lijeva. Usporedbom rezultata svojstava, na početku i kraju lijevanja, uočava se kako pri kraju lijevanja dolazi do smanjenja u mehaničkih svojstava. Analiza strukture ukazuje kako se radi o željeznom lijevu s pretežno feritnom osnovom. Prema kraju lijevanja postupno raste udio perlita.

Sažetak (engleski)

Ductile iron, or nodular cast iron, HRN-EN-GJS-400-15 is used in the automotive industry to make parts such as gears, differentials and axles due to its high strength and good toughness. Demands on quality are constantly growing, customers are setting higher and higher demands. In order for manufacturers to fulfill this, it is important to constantly control the chemical composition and minimize possible defects in the microstructure, and to modify production procedures in order to increase production and reduce costs. In this final paper, the production of ductile iron HRN-EN-GJS-400-15 is monitored, specifically the influence of the melt retention time in the casting ladle on the final quality of ductile iron. Two Y-shaped cast samples were cast in the production process. Chemical composition, mechanical properties and structure of nodular cast iron were tested. By comparing the results of the properties, at the beginning and end of casting, it is observed that near the end there is a drop in the mechanical properties. Analysis of the microstructure indicates that matrix of cast iron is predominantly ferrite base. Towards the end of the process, the proportion of pearlite gradually increases.

• Ključne riječi: nodularni lijev; mehanička svojstva; struktura; ferit; Y proba; grafit
• Ključne riječi (engleski): ductile iron; mechanical properties; structure; ferrite; Y-shaped cast samples; graphite
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:115:530295
• Studijski program: Naziv: Ljevarstvo; Vrsta studija: stručni; Stupanj studija: kratki; Akademski / stručni naziv: stručni/a pristupnik/ pristupnica ljevarstva (pristup.ljev.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2025-07-16
• Datum i vrijeme pohrane: 2024-07-02 11:42:33